Silica Mortar

Unshaped silica material


Silica Mortar(Unshaped silica material)
Introduction 
Refractory mortar is also as known as joint filler, it is composed of a certain particle ratio of refractory powder, binder and additive, pour water or liquid binder to tune into a paste. Silica mortar is an important part of refractory mortar which is as Cab-O-sil or adding some ganister sand as main raw materials, the binder adopts mild-clay or chemical bond.
Applications :
Silica mortar is mainly used for laying and repair of coke oven, hot blast stove, glass melting furnace, melting furnace and other masonry of high quality silica bricks industrial furnace. 
Mixing sequence:
1. The silica mortar is the fine powder (0.088mm). Put the mortar in to the mixer and spray the small bag of additives on the dry powder evenly, mix them for 3 to 5min. Next, put 32 to 35 per cent of clean water (tap water and water amount can be adjusted according to actual conditions) into it and continue mixing for 5 to 10min. The effect will be better if you put the mortar slurry static for 10min. Amount of agitation should be determined according to the capacity of mixer. But it must be used by the bag. 
2. The mortar well mixed should be used as soon as possible for fear of loosing effectiveness. 
Attention: it is prohibited to put the additives into the water separately; it is prohibited to use acid industrial waste water to mix the slurry; operate strictly according to the requirements, or else it will influence the masonry quality and useful life of the mortar.
Advantage :
1. High adhesive strength.
2. High refractoriness.
3. Excellent refractoriness under load.
4. Good installation performance.
Specifications :

Items Silica refractory mortar
Refractoriness (° C ≥1580 ≥1670 ≥1690 ≥1670 ≥1690 ≥1690 ≥1710 ≥1710
Bonding time(min) 1-2 1-2 1-2 1-2 1-2 1-2 1-2 1-2
Chemicalcomposing(%) SiO2 ≥85 ≥92 ≥94 ≥92 ≥94 ≥94 ≥94 ≥96
Al2O3 - - ≤1 - - ≤1 ≤0.5 ≤0.8
Fe2O3 - - - - - ≤1 ≤0.5 ≤0.7
Flexural bond strength(MPa) 110°C×24h ≥1 ≥1 ≥1 ≥0.5 ≥0.5 ≥0.8 - ≥0.8
1400°C×3h ≥3 ≥3 ≥3 ≥1.5 ≥1.5 ≥2 - ≥0.5
0.2Mparefractorinessunder
load 
(°C)
≥1420 ≥1500 ≥1600 - - ≥1600 ≥1650 ≥1620

Packaging and Delivery Time :
Our packing: 
1) Net weight 25kg per units(plastic woven bag); 1 metric ton in P.P bag(waterproofing) with sling.
2) Net weight 25kg per units(plastic woven bag); 1 metric ton on pallet with plastic film. 
3) As customer's request.
Delivery:10-30 days according to the quantity
 

Pre:Silica Mortar Next:end

Contact

Contacts:Helen

Mobile:+86-15032669189

TEL/FAX:+86-0311-82778868

Email:admin@xkrefractorybrick.com

SKYPE:silicabrick@hotmail.com hbxk@2016

Factory Address:The southern part of Beichengzhai Village, Xingtang Town,Shijiazhuang City, Hebei Province , China (Mainland)